General introduction on grade category, name, technical requirements, characteristics, application and description of resins:

191# Ortho-benzene common resin Appearance: light yellow transparent liquid, viscosity: 0.25-0.5Pa.s. Acid value: 18-34mgkoH/g. Gelation: 6-10min Solid content: 63%-68% Light color, fast curing , Good mechanical properties. Suitable for all kinds of ordinary FRP products.

192# low shrinkage resin Appearance: white viscous liquid, viscosity: 08-1 Pa.s. Acid value: 20-28mgkoH/g. Gelation: 10-14min solid content: 64%-66% general low shrinkage resin. It is suitable for FRP products with low deformation requirements.https://hotfrp.com/frp-windows-doors

196# Ortho-benzene common resin Appearance: light yellow transparent liquid, viscosity: 0.3-0.45 Pa.s. Acid value: 20-35 mgkoH/g. Gelation: 5-10min Solid content: 63%-69% Good impact resistance . It can be used to make car shells, bathtubs, cooling towers, and storage tanks. It can also be used for artificial marble and coexistence of steel and soft.

306# Ordinary resin Appearance: light yellow transparent liquid, viscosity: 0.3-0.5 Pa.s. Acid value: 16-30 mgkoH/g. Gelation: 7-11min, solid content: 60%-65%, high hardness, rigidity it is good. Used for general anti-corrosion of cooling tower, good water resistance, corrosion resistance of low concentration chemical medium, can be used as dilute acid container, sanitary ware, ship, etc.

189# Ortho-benzene common resin Appearance: light yellow transparent liquid, viscosity: 0.26-0.4 Pa.s. Acid value: 17-32mgkoH/g. Gelation: 6-12min, solid content: 60%-66%, water resistance, light resistance Corrosion, can be used for general anti-corrosion, making boats, boats and other water-based FRP products, especially with anti-corrosion effect on seawater, and can be used at 100°C.

3301# Bisphenol A corrosion-resistant type

Resin appearance: yellow-light brown liquid, viscosity: 0.3-0.6Pa.s. Acid value: 8-16mgkoH/g. Gelation: 5-15min, solid content: 58%-62%, with good corrosion resistance, especially For alkaline media, its heat resistance is high, generally at 120°C. It is used to make chemical containers, pipes, tanks, etc., and its heat resistance and mechanical properties are higher than those of ortho-benzene and iso-benzene type resins.

197# Bisphenol A corrosion-resistant resin Appearance: yellow liquid, viscosity: 0.3-0.7Pa.s. Acid value: 10-18mgkoH/g. Gelation: 6-12min, solid content: 59%-63% Its performance and use Basically similar to 3301#.

197E# epoxy modified corrosion-resistant resin Appearance: yellow liquid, viscosity: 0.35-0.6Pa.s. Acid value: 10-18mgkoH/g. Gelation: 6-12min, solid content: 60%-64%, good mechanical properties , Strong adhesion, high hardness, strong acid and alkali resistance, temperature resistance 130 ℃.

3301A# Corrosion-resistant resin Appearance: yellow-light brown liquid, viscosity: 0.4-0.8Pa.s. Acid value: 14-22mgkoH/g. Gelation: 15-30min, solid content: 62%-64% Good Corrosion resistance, especially acidic medium, heat-resistant temperature of 110 ℃.

196-P# low shrinkage resin Appearance: opaque white viscous liquid, viscosity: 0.6-0.8Pa.s. Acid value: 8-26mgkoH/g. Gelation: 8-14min, solid content: 63%-65%, low thousand classification Shrinkable resin, its linear shrinkage rate is seven thousandths. It is suitable for FRP products that require small deformation and low shrinkage.

199# isophthalic heat-resistant resin Appearance: yellow-brown liquid, viscosity: 0.3-0.5 Pa.s. Acid value: 16-24mgkoH/g. Gelation: 7-9min, solid content: 61%-65%, with good impact resistance Its chemical resistance and electrical properties are higher than that of o-benzene, which can meet the requirements of winding and hand lay-up process.

199A# benzene heat-resistant resin Appearance: yellow liquid, viscosity: 0.35-0.6 Pa.s. Acid value: 18-30mgkoH/g. Gelation: 5-10min, solid content: 62%-66%. It has good mechanical properties. Resistant to general chemical corrosion and temperature 120℃, suitable for chemical containers with strong acid resistance.

199C# benzene heat-resistant resin Appearance: yellow liquid, viscosity: 0.35-0.6 Pa.s. Acid value: 18-30mgkoH/g. Gelation: 5-10min, solid content: 62%-66%, has good mechanical properties, Resistant to general chemical corrosion and temperature 120℃, suitable for chemical containers with strong acid resistance.

198# Heat-resistant resin Appearance: light yellow liquid, viscosity: 0.6-1.2 Pa.s. Acid value: 20-28mgkoH/g. Gelation: 5-8min, solid content: 63%-68%, high crosslinking density, heat resistance The performance is better, and it is used to make heat-resistant general glass fiber reinforced plastic products.

198A# Isophthalic heat-resistant grease Appearance: light yellow liquid, viscosity: 0.35-0.5 Pa.s. Acid value: 18-25mgkoH/g. Gelation: 8-12min, solid content: 62%-65% with temperature resistance and Chemical resistance, used for winding and paste.

198B# Orthophthalic heat-resistant resin Appearance: yellow transparent liquid, viscosity: 0.6-0.8 Pa.s. Acid value: 24-32mgkoH/g. Gelation: 6-10min, solid content: 63%-68%, with heat resistance, Can be used at 100℃

3200# vinyl ester resin Appearance: yellow liquid, viscosity: 0.3-0.5Pa.s. Acid value: 10-26mgkoH/g. Gelation: 10-20min, solid content: 56%-62% is bisphenol A epoxy The vinyl ester resin modified with acrylic has both the basic properties of epoxy and the construction process of unsaturated polyester resin. It has excellent corrosion resistance and mechanical properties, and is suitable for making corrosion-resistant FRP.

3201# vinyl ester resin Appearance: brown liquid, viscosity: 0.35-0.55Pa.s. Acid value: 8-20mgkoH/g. Gelation: 10-22min Solid content: 55%-60% isocyanate modified acrylic ethylene Base ester resin has high toughness, low shrinkage, water resistance, acid resistance and alkali resistance, and has good air-drying properties. The use temperature is 110 ℃, and it can be used as anti-corrosion equipment.

3202# Vinyl ester resin Appearance: yellow transparent liquid, viscosity: 0.4-0.5Pa.s. Acid value: 10-20mgkoH/g. Gelation: 10-20min Solid content: 58%-64% It has excellent chemical resistance It can meet the requirements of a variety of molding processes, and can be used for corrosion-resistant linings, electrical insulation materials, and anti-corrosion equipment.

W-1# Vinyl ester resin Appearance: brown transparent liquid, viscosity: 0.2-0.4Pa.s. Acid value: 16-26mgkoH/g. Gelation: 20-40min, solid content: 59%-68% phenolic epoxy type Vinyl ester resin, equivalent to DOW Chemical Company Derakane, -470 resin, resistant to higher temperatures. Humidity can reach 120℃, dry energy can reach 150℃, and can be used as a lining for integral glass products that are resistant to some solvents and oxidizing media.

W2-2# Vinyl ester resin Appearance: yellow transparent liquid, viscosity: 0.25-0.55Pa.s. Acid value: 8-24mgkoH/g. Gelation: 6-25min, solid content: 56%-63%, with corrosion resistance Good, especially for alkali media, temperature resistance can be 110 ℃, suitable for making various corrosion resistance, integral glass fiber reinforced plastic equipment lining.

W2-3# Vinyl ester resin Appearance: brown transparent liquid, viscosity: 0.35-0.5Pa.s. Acid value: 12-21mgkoH/g. Condensation: 10-30min, solid content: 57%-63% epoxy fussy ethylene Base ester resin has good corrosion resistance, high temperature resistance, heat distortion temperature of 160°C, and is suitable for making all kinds of glass fiber reinforced plastic products with high corrosion resistance and high temperature resistance.

197C# High temperature resistant, high chlorine resin Appearance: yellow transparent liquid, viscosity: 0.4-0.6Pa.s. Acid value: 22-30mgkoH/g. Condensation: 8-16min Solid content: 58%-65% Hyteric acid type Resin is highly corrosive and heat resistant, resistant to acids, wet chlorine and oxidizing media. Oxygen vaporization temperature can reach 177℃, and it is flame retardant. It can be used in chlor-alkali and acidic industries.

117# Air-dry resin Appearance: yellow liquid, viscosity: 0.5-0.6Pa.s. Acid value: 16-25mgkoH/g. Gelation: 5-8min, solid content: 63%-68%, non-anaerobic, non-anaerobic Products made by interference from the interference of air and oxygen.

118# Air-dry resin Appearance: red-brown liquid, viscosity: 0.4-0.8Pa.s. Acid value: 14-26mgkoH/g. Gelation: 10-20min, solid content: 58%-64% in about half an hour, even No stickiness, suitable for occasions where polyester film is not easy to use, used in the production of gel coat resin and furniture paint.

6688# Special resin for furniture, piano and automobile Appearance: light yellow transparent liquid Viscosity: 0.5-0.8Pa.s. Acid value: 20-30mgkoH/g. Gelation: 10-17min Solid content: 59%-64% Orthophthalic type The resin has good rigidity and toughness, and is used for polyester furniture, pianos and various types of hand-laid glass fiber reinforced plastic products in automobiles.

M-162# Pressure-resistant, flame-retardant and antistatic resin Appearance: white paste liquid, viscosity: 0.6-1Pa.s. Acid value: 18-30mgkoH/g. Gelation: 15-30min, solid content: 62%-70% With durable pressure>40MPa surface resistance 1X106-108Ω oxygen index ≥32%, suitable for underground FRP products.

M-162A# Antistatic resin Appearance: yellow paste liquid, viscosity: 0.3-0.6Pa.s. Acid value: 24-35mgkoH/g. Gelation: 6-12min, solid content: 60%-65%, good strength, surface resistance It can reach 1×106Ω, which is suitable for making the ground of computer room and FRP products with electrostatic surface.

115# Anchoring agent resin Appearance: yellow-brown liquid, viscosity: 0.35-0.7Pa.s. Acid value: 22-34mgkoH/g. Gelation: 3-6min Solid content: 62%-66% Fast curing, long storage time , The pulling force is large, and it is used for the anchoring effect of the anchor rod (supporting column) in the mine.

195# Translucent resin. Appearance: colorless-light green transparent liquid, viscosity: 0.3-0.6Pa.s acid value: 24-32mgkoH/g. Condensation: 4-8min, solid content: 59%-67%, which is better The light stability, weather resistance and heat resistance, light transmittance of 80-86% can be used to make high light transmittance FRP materials.

193# Translucent flame-retardant resin Appearance: colorless-light green transparent liquid, viscosity: 0.3-0.5Pa.s. Acid value: 20-30mgkoH/g. Gelation: 5-10min, solid content: 60%-66% Steel products. Reactive flame-retardant resin: oxygen index ≥28% refractive index (25°C) 1.5430±0.0020, suitable for hand lay-up and mechanical methods to produce transparent flame-retardant FRP products.

802# flame retardant resin Appearance: white paste liquid, viscosity: 0.6-0.8Pa.s. Acid value: 18-30mgkoH/g. Gelation: 13-22min, solid content: 64%-71% additive flame retardant resin, The oxygen index is ≥34%, which is suitable for FRP products with flame retardant requirements.

H-802# Flame retardant resin Appearance: yellow liquid, viscosity: 0.3-0.55Pa.s. Acid value: 20-34mgkoH/g. Gelation: 10-16min, solid content: 60%-67% reactive flame retardant resin, Oxygen index ≥30%, good light transmittance, suitable for glass fiber reinforced plastic products such as lighting hoods that require flame retardancy.

182# Flexible resin Appearance: light yellow transparent liquid Viscosity: 0.4-0.8Pa.s. Acid value: 22-32mgkoH/g. Gelation: 10-25min Solid content: 68%-72% It has high elasticity, good toughness and bending strength It is large, and can improve the impact resistance of the product, and is suitable for making FRP products with flexibility requirements.

885# Marble resin Appearance: yellow liquid, viscosity: 0.9-1.6Pa.s. Acid value: 16-28mgkoH/g. Gelation: 9-16min, solid content: 64%-70%. Medium viscosity, low shrinkage phthalic type , Not easy to crack, anti-aging, suitable for manufacturing marble resin.

885A# Marble resin Appearance: yellow liquid, viscosity: 1.8-2Pa.s. Acid value: 18-28mgkoH/g. Gelation: 45-60min Solid content: 68%-75% Ortho-phthalic marble resin, with high solids, Low shrinkage, strong water resistance, used in sanitary ware, plates, etc.

886# Agate resin Appearance: light yellow-colorless transparent liquid, viscosity: 1.0-1.6Pa.s. Acid value: 17-26mgkoH/g. Gelation: 10-15min, solid content: 65%-72% phthalic resin, With high rigidity and low shrinkage, it is a dual-purpose resin for manufacturing artificial agate marble.

886A# Agate resin Appearance: light yellow-colorless transparent liquid, viscosity: 0.4-0.7Pa.s. Acid value: 20-27mgkoH/g. Gelation: 8-16min, solid content: 65%-70% o-phthalic type, with It has low shrinkage, anti-aging and strong water resistance.

198# Extrusion resin Appearance: light yellow-colorless transparent liquid, viscosity: 0.4-0.7Pa.s. Acid value: 20-27mgkoH/g. Gelation: 8-16min, solid content: 65%-70% phthalic resin , Can be used for general extrusion and other processes such as doors and windows, greenhouses, canopy poles, etc.

198A# Extrusion resin Appearance: yellow liquid, viscosity: 0.9-1.6Pa.s. Acid value: 10-22mgkoH/g. Gelation: 6-10min, solid content: 59%-64% isophthalic resin, high strength, Good corrosion resistance, used for extrusion and premix, and used to produce chemically resistant grilles.

198B# Extrusion resin Appearance: yellow-white liquid, viscosity: 0.5-0.8Pa.s. Acid value: 20-27mgkoH/g. Gelation: 6-9min, solid content: 58%-64% p-phenylene-isobenzene type Pultrusion of resin has higher heat distortion temperature, higher tensile strength and bending strength, and is suitable for manufacturing products that require high strength and good corrosion resistance.

198C# Extrusion resin Appearance: yellow liquid, viscosity: 0.5-0.9Pa.s. Acid value: 12-23mgkoH/g. Gelation: 5-8min, solid content: 58%-65% vinyl Ester resin has a high thermal deformation temperature and good physical properties. It is suitable for oil well tie rods and high pressure pumping pipes.

191C# Winding resin Appearance: light yellow transparent liquid Viscosity: 0.3-0.5Pa.s. Acid value: 25-34mgkoH/g. Gelation: 8-16min Solid content: 64%-70% Ortho-phthalic winding resin, suitable for Glass fiber and other glass fiber reinforced plastic pipes and storage tank products.

199C# Winding resin Appearance: yellow liquid, viscosity: 0.35-0.6Pa.s. Acid value: 13-22mgkoH/g. Gelation: 10-20min Solid content: 60%-65%. Isophthalic winding resin for its water resistance , Good chemical resistance and high temperature resistance.

197C# Winding resin Appearance: yellow liquid, viscosity: 0.3-0.6Pa.s. Acid value: 8-16mgkoH/g. Gelation: 16-15min, solid content: 58%-61% bisphenol A resin, alkali resistance Strong, high strength, high temperature resistance, suitable for chemically resistant winding pipes, tanks, etc.

3201C# Winding resin Appearance: yellow transparent liquid, viscosity: 0.3-0.5Pa.s. Acid value: 10-18mgkoH/g. Gelation: 12-18min, solid content: 64%-68% vinyl ester type, temperature resistant, It has high corrosion resistance and high impact resistance. It is used for the lining of winding pipes and tanks.

189# Marine resin Appearance: yellow-light brown transparent liquid, viscosity: 0.3-0.6Pa.s. Acid value: 10-24mgkoH/g. Gelation: 14-20min Solid content: 58%-65% m-phenylene marine resin has Seawater resistance, high strength, suitable for making boats, boats and other water tools.

189A# Marine resin Marine resin Appearance: yellow liquid, viscosity: 0.4-0.8Pa.s. Acid value: 10-26mgkoH/g. Gelation: 6-15min Solid content: 59%-64% m-phenylene/neopentyl glycol Type marine resin, its performance is better than MSS-618#.

199M# Mold resin appearance: yellow-light brown liquid viscosity: 0.8-1.4Pa.s. acid value: 9-20mgkoH/g. gelation: 8-15min solid content: 59%-65% isophthalic resin, with High strength, low shrinkage, high smoothness and other characteristics, suitable for making various molds.

191E# Ortho-phthalic thixotropic resin view: light yellow-white liquid, viscosity: 0.8-1Pa.s. gelling: 10-20min thixotropic: 2.5-4 spray, hand lay-up thixotropic resin, can quickly penetrate, on the slope No glue flow occurs on the surface, and it is suitable for making products that are not easy to use polyester film.

199E# Isophthalic thixotropic resin Appearance: light yellow-white liquid Viscosity: 0.9-1.2Pa.s. Gelation: 12-22min Thixotropy: 2.5-3.5

199F# M-phenylene thixotropic resin Appearance: light yellow-white viscous liquid, viscosity: 2.5-3.2Pa.s. Gelation: 5-18min, thixotropy: 4.5-6.5

D-33 anticorrosive resin monomer appearance: white solid, melting point: 54-62°C. Hydroxyl value: 8.4-9.3, refractive index: 1.5568-1.5600, free phenol: 0.01-0.05% Use Tiansheng 3301#, 197#, 323#, etc. The raw material of bisphenol A resin.